High Rate Deposition of Microcrystalline Silicon Solar Cells Using 13.56 MHz PECVD – Prerequisites and Limiting Factors
- 1 January 2002
- journal article
- Published by Springer Nature in MRS Proceedings
Abstract
Microcrystalline silicon (μìc-Si:H) solar cells were prepared in a wide range of deposition parameters using high pressure 13.56 MHz plasma-enhanced chemical vapor deposition (PECVD). Focus was on the influence of deposition pressure, electrode distance and the application of a pulsed plasma on high rate deposition of solar cells. At electrode distances between 5 and 20 mm solar cells with efficiencies >8 % were prepared. A medium electrode distance of 10 mm yielded best device performance. Pulsed plasma deposition leads to good results at medium deposition rates of ∼5 Å/s, for higher rates a strong decrease of efficiency was observed. The highest efficiencies in a small area reactor were 8.9 % for CW and 8.4 % for pulsed plasma. We also succeeded in preparing μc-Si:H and a-Si:H/μc-Si:H solar cells in a 30x30 cm2 reactor with efficiencies of 9 % and 12.5 %, respectively.Keywords
This publication has 11 references indexed in Scilit:
- Optical emission spectroscopy study toward high rate growth of microcrystalline siliconThin Solid Films, 2001
- Cost effective and high-performance thin film Si solar cell towards the 21st centurySolar Energy Materials and Solar Cells, 2001
- Microcrystalline/micromorph silicon thin-film solar cells prepared by VHF-GD techniqueSolar Energy Materials and Solar Cells, 2000
- High rate growth of microcrystalline silicon using a high-pressure depletion method with VHF plasmaSolar Energy Materials and Solar Cells, 2000
- Intrinsic microcrystalline silicon: A new material for photovoltaicsSolar Energy Materials and Solar Cells, 2000
- Texture etched ZnO:Al coated glass substrates for silicon based thin film solar cellsThin Solid Films, 1999
- Particle Growth Kinetics in Silane RF DischargesJapanese Journal of Applied Physics, 1999
- Particle formation and a-Si:H film deposition in narrow-gap RF plasma CVDThin Solid Films, 1999
- High Rate Deposition of Microcrystalline Silicon Using Conventional Plasma-Enhanced Chemical Vapor DepositionJapanese Journal of Applied Physics, 1998
- High deposition rate amorphous and polycrystalline silicon materials using the pulsed plasma and “Hot-Wire” CVD techniquesSolar Energy Materials and Solar Cells, 1998