Evolution of vacancy ordering and defect structure in epitaxial YSi2−x thin films on (111)Si
- 1 April 1992
- journal article
- research article
- Published by AIP Publishing in Journal of Applied Physics
- Vol. 71 (7) , 3307-3312
- https://doi.org/10.1063/1.350950
Abstract
The evolution of vacancy ordering and defect structure in epitaxial YSi2−x thin films on (111)Si have been studied by both conventional and high‐resolution transmission electron microscopy. Epitaxial YSi2−x with an ordered vacancy structure was grown on (111)Si by rapid thermal annealing. In samples annealed at 500 °C for 120 s epitaxial YSi2−x was found to form. After annealing at 600 °C for 15 s, the appearance of additional diffraction spots is attributed to the formation of an ordered vacancy superstructure in the epitaxial YSi2−x thin films. In samples annealed at 600 °C for longer time or higher temperatures, the splitting of extra diffraction spots is correlated to the formation of an out‐of‐step structure. Streaking of the split diffraction spots in the diffraction pattern is attributed to the presence of an out‐of‐step structure with a range of M values. The M was found to settle down to 2 after high‐temperature and/or long time annealing. Planar defects in YSi2−x films were analyzed to be stacking faults on {101̄0} planes with 1/6 〈1̄21̄3〉 displacement vectors. Computer simulation was carried out to determine the atomic structure of stacking fault. The simulated images are seen to match rather well with experimental images taken under two different values of defocus.This publication has 25 references indexed in Scilit:
- Epitaxial growth of transition-metal silicides on siliconMaterials Science Reports, 1991
- Low temperature phase separation in CeSi1.86Journal of Materials Research, 1990
- Extremely low resistivity erbium ohmic contacts to n-type siliconApplied Physics Letters, 1989
- Fabrication and structure of epitaxial Er silicide films on (111) SiApplied Physics Letters, 1989
- Epitaxial growth of rare-earth silicides on (111) SiApplied Physics Letters, 1986
- The Schottky-barrier height of the contacts between some rare-earth metals (and silicides) and p-type siliconApplied Physics Letters, 1981
- Low Schottky barrier of rare-earth silicide on n-SiApplied Physics Letters, 1981
- Contact reaction between Si and rare earth metalsApplied Physics Letters, 1981
- Diffusion marker experiments with rare-earth silicides and germanides: Relative mobilities of the two atom speciesJournal of Applied Physics, 1981
- The formation of silicides from thin films of some rare-earth metalsApplied Physics Letters, 1980