Effect of Grain‐Boundary Oxidation on Fracture Toughness of SiC
- 1 August 1987
- journal article
- Published by Wiley in Journal of the American Ceramic Society
- Vol. 70 (8) , 548-552
- https://doi.org/10.1111/j.1151-2916.1987.tb05703.x
Abstract
No abstract availableKeywords
This publication has 17 references indexed in Scilit:
- Oxygen penetration into silicon carbide ceramics during oxidationCeramics International, 1985
- Intergranular Crack‐Deflection Toughening in Silicon CarbideJournal of the American Ceramic Society, 1983
- Strength Distributions of SiC Ceramics After Oxidation and Oxidation Under LoadJournal of the American Ceramic Society, 1981
- Boron Redistribution in Sintered α‐SiC During Thermal OxidationJournal of the American Ceramic Society, 1981
- Fracture Toughness and High‐Temperature Slow Crack Growth inSiCJournal of the American Ceramic Society, 1980
- KIcand Delayed Fracture Measurements on Hot‐Pressed SiCJournal of the American Ceramic Society, 1979
- Crack propagation and fracture in silicon carbideJournal of Materials Science, 1975
- Effect of Alumina Content on the Oxidation of Hot‐Pressed Silicon CarbideJournal of the American Ceramic Society, 1975
- The Oxidation of Silicon Carbide at 1150° to 1400°C and at 9 × 10[sup ?3] to 5 × 10[sup ?1] Torr Oxygen PressureJournal of the Electrochemical Society, 1966
- Determination of Percent Crystallinity of Partly Devitrified Glass by X‐Ray DiffractionJournal of the American Ceramic Society, 1962