Growth of epitaxial silicon layers by vacuum evaporation

Publisher Website
Google Scholar
Abstract
Epitaxial Si layers have been grown on (111) Si substrates by the vacuum evaporation method. A preliminary assessment of these layers was recently reported (Unvala and Booker 1964, Paper I). The present paper describes a transmission electron microscope investigation of the initial nucleation and growth process. The layers examined were grown using an initial pressure of 3 × 10−6 mm Hg, a substrate temperature of 1200°c and deposition rates in the range 0·1 to 2·5 micron/min. Three different types of growth were distinguished. At slow rates ( 1·0 micron/min), no growth centres were observed from the earliest stages, and no stacking faults occurred in any areas of the layer. A qualitative explanation is proposed to account for these observations. In particular, it is considered that (a) the separate growth centres form, and the stacking faults occur, because of contamination present on the substrate surface, and (b) the growth rate dependence arises because the incident Si atoms are able to act as a getter and remove the contamination, and the effectiveness of the gettering action increases as the deposition rate increases.