Low electric field breakdown of thin SiO/sub 2/ films under static and dynamic stress
- 1 May 1997
- journal article
- Published by Institute of Electrical and Electronics Engineers (IEEE) in IEEE Transactions on Electron Devices
- Vol. 44 (5) , 801-808
- https://doi.org/10.1109/16.568042
Abstract
A comprehensive study of Time-Dependent Dielectric Breakdown (TDDB) of 6.5-, 9-, 15-, and 22-nm SiO/sub 2/ films under dc and pulsed bias has been conducted over a wide range of electric fields and temperatures. Very high temperatures were used at the wafer level to accelerate breakdown so tests could be conducted at electric fields as low as 4.5 MV/cm. New observations are reported for TDDB that suggest a consistent electric field and temperature dependence for intrinsic breakdown and a changing breakdown mechanism as a function of electric field. The results show that the logarithm of the median-test-time-to failure, log (t/sub 50/), is described by a linear electric field dependence with a field acceleration parameter that is not dependent on temperature. It has a value of approximately 1 decade/MV/cm for the range of oxide thicknesses studied and shows a slight decreasing trend with decreasing oxide thickness. The thermal activation E/sub a/ ranged between 0.7 and 0.95 eV for electric fields below 9.0 MV/cm for all oxide thicknesses. TDDB tests conducted under pulsed bias indicate that increased dielectric lifetime is observed under unipolar and bipolar pulsed stress conditions, but diminishes as the stress electric field and oxide thickness are reduced. This observation provides new evidence that low electric field aging and breakdown is not dominated by charge generation and trapping.Keywords
This publication has 25 references indexed in Scilit:
- Time dependent dielectric breakdown at 210 AA oxidesPublished by Institute of Electrical and Electronics Engineers (IEEE) ,2003
- A new physics-based model for time-dependent-dielectric-breakdownPublished by Institute of Electrical and Electronics Engineers (IEEE) ,1996
- Oxide and interface degradation and breakdown under medium and high field injection conditions: A correlation studyMicroelectronic Engineering, 1995
- Field and temperature acceleration of time-dependent dielectric breakdown in intrinsic thin SiO/sub 2/Published by Institute of Electrical and Electronics Engineers (IEEE) ,1994
- High field emission related thin oxide wearout and breakdownPublished by Institute of Electrical and Electronics Engineers (IEEE) ,1994
- A lifetime projection method using series model and acceleration factors for TDDB failures of thin gate oxidesPublished by Institute of Electrical and Electronics Engineers (IEEE) ,1993
- Time-dependent dielectric breakdown characteristics of N/sub 2/O oxide under dynamic stressingIEEE Electron Device Letters, 1992
- On the breakdown statistics of very thin SiO2 filmsThin Solid Films, 1990
- A numerical analysis for the small-signal response of the MOS capacitorSolid-State Electronics, 1989
- Electrical breakdown in thin gate and tunneling oxidesIEEE Transactions on Electron Devices, 1985